Refine
Publication Type
- Article (6)
- Conference Proceeding (2)
Laser shock peening is a new and important surface treatment technique that can enhance the mechanical properties of metal materials. Normally, the nanosecond laser with pulse-width between 5 ns and 20 ns is used to induce a high-pressure shock wave that can generate plastic deformation in the top layer of metals. The femtosecond laser shock peening in the air has been studied recently, which can induce higher pressure shock wave than that of traditional nanosecond laser shock peening in a very short time. The NiTi alloy is processed by femtosecond laser shock peening, then a nanoindentation device is used to measure its surface hardness and residual stress. The hardness results of NiTi alloy before and after treatment show that the femtosecond laser shock peening can increase the hardness of NiTi alloy, which also shows that the femtosecond laser can be used to perform laser shock peening on NiTi alloy without coating.
The laser nitriding was performed in nitrogen gas at room temperature (20 °C) and low temperature (−190 °C) by a low power fiber laser to modify the wear and abrasion resistance of NiTi alloy. The surface roughness and element composition were analyzed by roughness device and energy-dispersive X-ray spectroscopy respectively. The results of roughness show that laser treatment can change the surface roughness due to the laser remelting. The effect of laser nitriding on the microhardness, friction coefficient, and worn scars of NiTi alloy was also studied, which shows that the microhardness of the NiTi alloy increases after laser nitriding. The optical microscope and scanning electron microscope were used to characterize the surface of NiTi alloy after wear testing to observe the microstructure of worn scars. The results show that the laser nitriding with different parameters can induce a nitride layer with different thicknesses and the higher energy deposition is the key factor for the formation of the nitride layer, which can decrease the friction coefficient and reduce wear loss during the application of NiTi alloy. The improvement of wear resistance can be attributed to the hard nitriding layer.
Laser shock peening with a femtosecond laser system was presented in this research work. The NiTi shape memory alloy was processed by the femtosecond laser shock peening (FsLSP) treatment without a protective layer in the air. Femtosecond laser shock peening is a new surface technology, which can induce an intense shock wave with low single laser pulse energy under atmospheric conditions. The surface topography, roughness, microhardness, and wear resistance were measured on the surface of NiTi alloy before and after femtosecond laser peening treatment. The results showed that the surface roughness and microhardness could be increased after femtosecond laser shock peening, which may be due to the laser ablation and micro-plastic deformation induced by the shock wave. The wear property of NiTi alloy was improved, which may be attributed to the FsLSPed surface texturing and …
High strength steel has been used in the aviation industry and automotive body structural applications to reduce its mass through a reduction in thickness. Therefore, it is very important to enhance its mechanical property, such as microhardness. In the present research, the high strength steel samples were treated by laser shock peening (LSP) with different laser pulse energy and laser pulse width. The microhardness and residual stress were measured to compare the difference between laser energy of 3 J with 10 ns and 5 J with 20 ns. The results in the study show that the surface LSP treatment can increase the microhardness and the compressive residual stress can be found when the samples were tested by hole drilling testing.
The experiment study presents the influence of femtosecond laser shock peening (FsLSP) without a protective layer in the air on the surface hardness and surface mechanical property of NiTi shape memory alloy. Femtosecond laser shock peening is a new possibility of direct laser ablation without any protective layer under atmospheric conditions, which can produce intense shock waves with low pulse energy in the air. The average surface roughness values of the NiTi alloy samples were measured, because the surface roughness may affect its friction resistance. The results showed that the surface roughness of NiTi increased after femtosecond laser shock peening treatment. In comparison with the initial state, the coefficient of friction decreased and surface microhardness increased after femtosecond laser shock peening treatment with different FsLSP parameters. This improvement of wear properties may be attributed to the enhancement of surface microhardness and surface titanium oxide layer induced by the shock wave and laser ablation during FsLSP treatment.
Laser shock peening with femtosecond laser was used to improve the corrosion resistance of biomedical NiTi alloy without protective coating in the air environment. The energy dispersive X-ray analysis (EDX) and X-ray diffraction (XRD) based analysis showed that the laser ablation could produce titanium oxide layer and femtosecond laser shock peening (FsLSP) can generate residual stress in the surface layer of NiTi alloy. The FsLSP improved the corrosion resistance of NiTi in 3.5% NaCl solution and Hank’s solution and also prevented the formation of corrosion cracks and pits during corrosion testing. The reasons for the improvement of corrosion behavior may be the generation of residual stress and titanium oxide film during the laser surface treatment.
This research paper presents the attempt at ultrashort pulsed laser shock peening with absence of absorptive layer and confining medium which could enhance surface microhardness and the abrasion property of NiTi shape memory alloy. The average roughness values of NiTi specimen were measured on the surface, because the roughness would affect the friction resistance. The microhardness and Young's modulus were investigated at different position of single laser spot by nanoindentation technique. The pin-on-plate sliding abrasion testing were performed with different load-force (0.5 N and 2 N) for different testing time. Results showed that ultrashort pulsed laser shock peening treatment would cause a significant improvement on friction coefficient and abrasion property, which was attributed to the change of surface modification, such as roughness, microhardness, microstructure and titanium oxide layer …