Refine
Year
- 2021 (30) (remove)
Publication Type
- Article (20)
- Conference Proceeding (10)
Keywords
- active optics (2)
- adaptive optics (2)
- deformable mirror (2)
- space telescopes (2)
- Hilfsmittelbranche (1)
- MDR (1)
- Medical Device Regulation (1)
- Medizinprodukte (1)
- Photoluminescence (1)
- Pr3+ luminescence (1)
Faculty
- Physikingenieurwesen (PHY) (30) (remove)
The Anatomy of Glenoid Concavity-Bony and Osteochondral Assessment of a Stability-Related Parameter
(2021)
The laser nitriding was performed in nitrogen gas at room temperature (20 °C) and low temperature (−190 °C) by a low power fiber laser to modify the wear and abrasion resistance of NiTi alloy. The surface roughness and element composition were analyzed by roughness device and energy-dispersive X-ray spectroscopy respectively. The results of roughness show that laser treatment can change the surface roughness due to the laser remelting. The effect of laser nitriding on the microhardness, friction coefficient, and worn scars of NiTi alloy was also studied, which shows that the microhardness of the NiTi alloy increases after laser nitriding. The optical microscope and scanning electron microscope were used to characterize the surface of NiTi alloy after wear testing to observe the microstructure of worn scars. The results show that the laser nitriding with different parameters can induce a nitride layer with different thicknesses and the higher energy deposition is the key factor for the formation of the nitride layer, which can decrease the friction coefficient and reduce wear loss during the application of NiTi alloy. The improvement of wear resistance can be attributed to the hard nitriding layer.
Laser shock peening is a new and important surface treatment technique that can enhance the mechanical properties of metal materials. Normally, the nanosecond laser with pulse-width between 5 ns and 20 ns is used to induce a high-pressure shock wave that can generate plastic deformation in the top layer of metals. The femtosecond laser shock peening in the air has been studied recently, which can induce higher pressure shock wave than that of traditional nanosecond laser shock peening in a very short time. The NiTi alloy is processed by femtosecond laser shock peening, then a nanoindentation device is used to measure its surface hardness and residual stress. The hardness results of NiTi alloy before and after treatment show that the femtosecond laser shock peening can increase the hardness of NiTi alloy, which also shows that the femtosecond laser can be used to perform laser shock peening on NiTi alloy without coating.
Cross-saturation of the gain media in intra-cavity pumped lasers leads to complex dynamics of the laser power. We present experimental results and a detailed theoretical analysis of this nonlinear dynamics for an intra-cavity pumped Yb:YAG thin-disk laser in the framework of a rate-equation model. The gain medium of this laser is residing in the resonator of a conventional, diode-pumped Yb:YAG thin-disk laser. Continuous-wave operation, periodic pulse trains, and chaotic fluctuations of the optical power of both lasers were observed. The dynamics is not driven by external perturbations but arises naturally in this laser system. Further examination revealed that these modes of operation can be controlled by the resonator length of the diode-pumped laser but that the system can also show hysteresis and multi-stability.
This work deals with the spectroscopic properties of praseodymium doped single crystalline lutetium aluminum garnet (LuAG:Pr3+). A special focus was set on temperature- and time-dependent spectroscopy. Beyond the well-known down-conversion luminescence of LuAG:Pr3+, also UV-A/B up-conversion luminescence under excitation with a 488 nm laser was thoroughly investigated. Furthermore, the results of the spectroscopic investigations on the single crystalline material were supplemented and compared with measurements on a microscale powder sample.
In addition, to the spectroscopic investigations, mechanistic considerations are presented to obtain a closer look at the up-conversion process in LuAG:Pr3+. We promote the thesis of a temperature-dependent energy transfer up-conversion mechanism.